Abstract
High Velocity Oxygen Fuel (HVOF) spray is being widely used in many industries to deposit erosion-resistant coatings or restore the dimension for components. The porosity, adhesion strength, and hardness are the essential properties commonly used to access the quality of coatings and thus the effectiveness of a HVOF spray process. To achieve desired coating properties and reduce production cost, optimization of process parameters in HVOF spray has developed immensely during last decades. Among the spray parameters, particle velocity, powder feed rate and standoff distance contribute a significant influence on the final properties of the coatings. In the present study, experiments of HVOF thermal spray were prepared for the 67Ni18Cr5Si4B alloy powder. The process parameters including spray velocity, powder feed rate and spray distance were optimized for the objectives of adhesion strength, porosity and microhardness of 67Ni18Cr5Si4B coating. Based on the Taguchi method, signal-to-noise (S/N) ratio and overall evaluation criteria (OEC) are determined to solve the optimization problem considering multiple performance characteristics. Moreover, analysis of variance (ANOVA) was conducted to analyse the contribution percentage of each process parameter. The optimal process parameters in HVOF spray of 67Ni18Cr5Si4B were found for the multi-response optimization as velocity of 1000 m/s, powder feed rate of 30 g/min, and spray distance of 0.2 m. The results of ANOVA indicated that the spray distance was the most significant parameter affecting the output spray quality among the investigated process parameters, subsequently to the powder flow rate and velocity of spray. Finally, a confirmatory experiment was carried out to support the accuracy of optimal process parameters.
Disclosure statement
No potential conflict of interest was reported by the authors.